Metal press parts without fracture surfaces produced by fine blanking processing.
Parts processed by fine blanking can achieve superior shape accuracy and flatness compared to parts processed by general pressing. Additionally, the cut surface allows for a smooth surface without fractures. This significantly enhances the functionality of the product.
![[Example] Gas nitriding (heat treatment) of clutch plates](https://image.mono.ipros.com/public/product/image/eb3/2000317802/IPROS6019444903927902524.PNG?w=280&h=280)
Case of heat treatment "gas soft nitriding treatment" for automotive parts "clutch plate".
This is an introduction to the case of heat treatment "gas nitriding" for automotive clutch components, specifically "clutch plates." We can accommodate gas nitriding with materials provided. ITEC's gas nitriding results in a clean finish due to air cooling. 【Processing Details】 Thickness: 1.2mm, Material: SPCC-8B Gas Nitriding *For more details, please refer to the PDF available for download.
![[Example] Wire cut and heat treatment for "clutch plate" for racing bikes.](https://image.mono.ipros.com/public/product/image/313/2000317806/IPROS5424231444200629771.PNG?w=280&h=280)
Flatness below 0.02! Introduction of examples of wire cut and heat-treated "clutch plates" for racing bikes.
This is an introduction to the case of wire cutting and heat treatment for the "clutch plate" used in Moto GP racing bikes. The process design takes into account heat treatment distortion, keeping flatness to 0.02 or less. Additionally, the between diameter is within ±0.05. 【Processing Details】 Product Name: Clutch Plate for Racing Bikes Lot: 1 piece Flatness: 0.02 or less Between Diameter: ±0.05 or less *For more details, please refer to the PDF available for download.
Introduction of case studies on nitriding hardening (low distortion heat treatment) for automotive parts "clutch plates".
This is an introduction to the case of nitriding hardening (low distortion heat treatment) for automotive parts "clutch plate (SPCC)." The thickness varies by part number, ranging from t=1.0 to 4.0, with the material being SPCC. Additionally, nitriding hardening treatment is also possible for other materials such as SCM. A notable feature is that the heat treatment distortion is less than half that of carburizing nitriding, and while conventional carburizing nitriding required flatness correction afterward, nitriding hardening does not require this due to its low distortion. 【Details of the case】 Product name: Clutch plate Lot: 1000 pieces Specifications: Hardness HV800 or higher, depth 0.04mm (actual) *For more details on nitriding hardening, please refer to the PDF available for download.
![[Example] Precision Shearing Press SPCC Carburizing and Nitriding Treatment Integrated Support](https://image.mono.ipros.com/public/product/image/bb5/2000317799/IPROS3853540862700905403.PNG?w=280&h=280)
A case of integrated production from mold design of automotive parts clutch plates to precision shearing and carburizing-nitriding treatment.
This is an introduction to a case of integrated production from mold design, precision shearing, to carburizing and nitriding treatment for automotive parts clutch plates. The thickness varies by part number, ranging from t=1.0 to 4.0, with a material of SPCC. 【Processing Details】 Product Name: Clutch Plate Lot: 500 to 50,000 pieces/month Press processing dimensional accuracy: 5/100, and the accuracy after heat treatment is ±0.1 *For more details, please refer to the PDF available for download.